Product name：ESD Nylon Compound
Product model：Nylon ESD Compound
Product brand：INCHR
Processing customized：Antistatic Plastic Compound
Product specification：Surface Resistivity 10^3~10^5 Ohms
Product description：ESD C 203 A
Nylon 6 (PA)
Glass Fiber
Electrically Conductive
ESD Protection
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCEEnglish SI Metric ASTM
TESTPrimary Additive 20 % 20 % Specific Gravity 1.31 1.31 D 792 Molding Shrinkage 1/8 in (3.2 mm) section 0.0020 - 0.0040 in/in 0.20 - 0.40 % D 955
MECHANICALImpact Strength, Izod notched 1/8 in (3.2 mm) section 1.5 ft-lbs/in 80 J/m D 256 unnotched 1/8 in (3.2 mm) section 10.0 ft-lbs/in 534 J/m D 4812 Tensile Strength 15000 psi 103 MPa D 638 Tensile Elongation 1.0 - 3.0 % 1.0 - 3.0 % D 638 Tensile Modulus 0.85 x 10^6 psi 5861 MPa D 638 Flexural Strength 25000 psi 172 MPa D 790 Flexural Modulus 0.75 x 10^6 psi 5171 MPa D 790
ELECTRICALVolume Resistivity < 1E3 ohm.cm < 1E3 ohm.cm D 257 Surface Resistivity < 1E6 ohm/sq < 1E6 ohm/sq D 257
ESD STM11.11Surface Resistance < 1E5 ohm < 1E5 ohm ESD STM11.11 Static Decay MIL-PRF-81705D, 5kV to 50 V, 12% RH < 2.00 s < 2.00 s FTMS101C
4046.1PROPERTY NOTES Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
GENERAL PROCESSING FOR INJECTION MOLDINGEnglish SI Metric Injection Pressure 10000 - 15000 psi 69 - 103 MPa Melt Temperature 470 - 535 °F 243 - 279 °C Mold Temperature 130 - 200 °F 54 - 93 °C Drying 2 hrs @ 180 °F 2 hrs @ 82 °C Moisture Content 0.20 % 0.20 % Dew Point 0 °F -18 °C
PROCESSING NOTESDesiccant Type Dryer Required.
30 Sep 2004 LCR
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.
Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.