产品名称:ESD C 1200 T-85A
订购热线:18820179977(微信同号)
产品说明:ESD C 1200 T-85A
Ether-based Thermoplastic Polyurethane Elastomer (TPUR/TPU)
ESD Protection
Electrically Conductive
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCEEnglish SI Metric ASTM
TESTSpecific Gravity 1.23 1.23 D 792 Molding Shrinkage 1/8 in (3.2 mm) section 0.0100 - 0.0150 in/in 1.00 - 1.50 % D 955
MECHANICALImpact Strength, Izod notched 1/8 in (3.2 mm) section No Break No Break D 256 unnotched 1/8 in (3.2 mm) section No Break No Break D 4812 Tensile Strength Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) 2200 psi 15 MPa D 412 Tensile Elongation Break, Die C, 0.125 in, 20 in/min (3.2mm, 500 mm/min) > 300.0 % > 300.0 % D 412 Tensile Stress Die C 0.125 in, 20 in/min (3.2 mm, 500 mm/min) @ 100 % 1800.0 psi 12.4 MPa D 412 Tear Strength, Die C 550.0 pli 96.4 N/mm D 624 Hardness Shore A, 10 s delay 90 90 D 2240 Shore D, instantaneous 45 45 D 2240
ELECTRICALVolume Resistivity < 1E3 ohm.cm < 1E3 ohm.cm D 257 Surface Resistivity < 1E6 ohm/sq < 1E6 ohm/sq D 257
ESD STM11.11Surface Resistance < 1E5 ohm < 1E5 ohm ESD STM11.11 Static Decay MIL-PRF-81705D, 5kV to 50 V, 12% RH < 2.00 s < 2.00 s FTMS101C
4046.1PROPERTY NOTES Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.
GENERAL PROCESSING FOR INJECTION MOLDINGEnglish SI Metric Injection Pressure 10000 - 15000 psi 69 - 103 MPa Melt Temperature 365 - 425 °F 185 - 218 °C Mold Temperature 100 - 140 °F 38 - 60 °C Drying 6 hrs @ 225 °F 6 hrs @ 107 °C Moisture Content 0.01 % 0.01 % Dew Point 0 °F -18 °C
PROCESSING NOTESDesiccant Type Dryer Required.
2 Sep 2008 SAC
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.