产品名称:ESD 300 EM TFE 15(RTP公司)
订购热线:18820179977(微信同号)
产品说明:ESD 300 EM TFE 15
Polycarbonate (PC)
ESD Protection
Static Dissipative
Easy Molding
PTFE Lubricated
PROPERTIES & AVERAGE VALUES OF INJECTION MOLDED SPECIMENS
PERMANENCEEnglish
SI Metric
ASTM
TESTSpecific Gravity
1.30
1.30
D 792
Molding Shrinkage
1/8 in (3.2 mm) section
0.0060 - 0.0080 in/in
0.60 - 0.80 %
D 955
MECHANICALImpact Strength, Izod
notched 1/8 in (3.2 mm) section
1.1 ft-lbs/in
59 J/m
D 256
unnotched 1/8 in (3.2 mm) section
21.0 ft-lbs/in
1121 J/m
D 4812
Tensile Strength
8000 psi
55 MPa
D 638
Tensile Elongation
5.0 - 10.0 %
5.0 - 10.0 %
D 638
Tensile Modulus
0.35 x 10^6 psi
2413 MPa
D 638
Flexural Strength
12500 psi
86 MPa
D 790
Flexural Modulus
0.35 x 10^6 psi
2413 MPa
D 790
ELECTRICALVolume Resistivity
1E3 - 1E5 ohm.cm
1E3 - 1E5 ohm.cm
D 257
Surface Resistivity
1E5 - 1E10 ohm/sq
1E5 - 1E10 ohm/sq
D 257
ESD STM11.11Surface Resistance
1E4 - 1E9 ohm
1E4 - 1E9 ohm
ESD STM11.11
Static Decay
< 2.00 s
< 2.00 s
FTMS101C
4046.1
THERMALDeflection Temperature
@ 264 psi (1820 kPa)
260 °F
127 °C
D 648
Ignition Resistance*
Flammability**
HB @ 1/16 in
HB @ 1.5 mm
D 635
PROPERTY NOTES
Data herein is typical and not to be construed as specifications.
Unless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.* This rating is not intended to reflect hazards of this or any other material under actual fire conditions.
** Values per RTP Company testing.
GENERAL PROCESSING FOR INJECTION MOLDINGEnglish
SI Metric
Injection Pressure
10000 - 15000 psi
69 - 103 MPa
Melt Temperature
550 - 600 °F
288 - 316 °C
Mold Temperature
180 - 250 °F
82 - 121 °C
Drying
4 hrs @ 250 °F
4 hrs @ 121 °C
Moisture Content
0.02 %
0.02 %
Dew Point
-20 °F
-29 °C
PROCESSING NOTESDesiccant Type Dryer Required.
8 Nov 2005 TES
This information is intended to be used only as a guideline for designers and processors of modified thermoplastics. Because design and processing is complex, a set solution will not solve all problems. Observation on a “trial and error” basis may be required to achieve desired results.
Data are obtained from specimens molded under carefully controlled conditions from representative samples of the compound described herein. Properties may be materially affected by molding techniques applied and by the size and shape of the item molded. No assurance can be implied that all molded articles will have the same properties as those listed.
上一个产品:ESD 300 EM FR A(RTP公司)下一个产品:ESD 303 EM(RTP公司)